Mechanical and thermal characterization of a beet pulp-starch composite for building applications

Résumé

This work shows the making of a new bio-based material for building insulation from sugar beet pulp and potato starch. The material is both lightweight and ecofriendly. The influence of starch/ sugar beet pulp ratio (S/BP) is studied. Four binder mass dosages are considered, 10, 20, 30 and 40% (relative to the beet pulp). Samples are characterized in terms of absolute and bulk density, compressive and flexural strength, as well as thermal properties (thermal conductivity and thermal inertia). The compressive strength increases linearly with the S/BP mass ratio to reach 0.52 MPa and the compressive strain is 30%. The thermal conductivity is to around 0.070 W/m. K. The results obtained shows that increasing starch amount tends to decrease composite porosity but increases thermal conductivity and mechanical properties. Depending on the starch content, beet pulp composites have a good thermal and can be used as building materials.
Fichier principal
Vignette du fichier
e3sconf_enviro2018_08005.pdf (710.13 Ko) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03556890 , version 1 (18-06-2024)

Identifiants

Citer

Hamzé Karpaky, Chadi Maalouf, Christophe Bliard, Alexandre Gacoin, Mohammed Lachi, et al.. Mechanical and thermal characterization of a beet pulp-starch composite for building applications. E3S web of conferences, 2019, REIMS, France. pp.08005, ⟨10.1051/e3sconf/20198508005⟩. ⟨hal-03556890⟩
13 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More