Investigation of Mn-Fe magnetic interaction in mechanically alloyed Fe doped-MnAlC by 57Fe Mössbauer spectrometry - Cnam - Conservatoire national des arts et métiers Accéder directement au contenu
Article Dans Une Revue Journal of Magnetism and Magnetic Materials Année : 2023

Investigation of Mn-Fe magnetic interaction in mechanically alloyed Fe doped-MnAlC by 57Fe Mössbauer spectrometry

Résumé

Four samples γ2-Mn40Fe0.5Al59.5, β-Mn60Fe0.5Al39.5, and ε-Mn50.5Fe0.5Al47C2, τ-Mn50.5Fe0.5Al47C2 were synthe- sized by mechanical alloying method. X-ray diffraction results showed high purity of the γ2, β, ε, and τ phases in each sample. M ̈ossbauer measurement at room temperature showed non-ferromagnetic characteristic of the γ2- Mn40Fe0.5Al59.5, β-Mn60Fe0.5Al39.5, and ε-Mn50.5Fe0.5Al47C2. Interestingly, τ-Mn50.5Fe0.5Al47C2 showed a complex magnetic hyperfine splitting, indicating magnetic ordered structure. The hyperfine interaction in τ-Mn50.5Fe0.5Al47C2 was found dependent with temperature, in which isomer shift (IS) and magnetic hyperfine field (Bhf) decreased with increasing temperature. From the IS temperature dependence curve, the Debye tem- perature (θD) is determined to be 422 ± 80 K. The temperature dependence of Bhf values and the thermomagnetic measurement yielded a Curie temperature (Tc) values of 560 ± 13 K and 565 ± 2 K respectively. In order to investigate the magnetic interaction between Fe and Mn atoms in τ-Mn50.5Fe0.5Al47C2, local magnetic order of τ-Mn50.5Fe0.5Al47C2 was probed by using in-field 57Fe M ̈ossbauer spectrometry. The obtained results showed that Fe and Mn formed a non-collinear magnetic structure with magnetic moments of Fe at different sites showing different canting angles with neighboring Mn atoms.
Fichier principal
Vignette du fichier
SSRN-id4206771.pdf (962.09 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04164841 , version 1 (15-11-2023)

Licence

Copyright (Tous droits réservés)

Identifiants

Citer

Van Tang Nguyen, Frédéric Mazaleyrat, Nirina Randrianantoandro. Investigation of Mn-Fe magnetic interaction in mechanically alloyed Fe doped-MnAlC by 57Fe Mössbauer spectrometry. Journal of Magnetism and Magnetic Materials, 2023, 568, pp.1-9. ⟨10.1016/j.jmmm.2023.170437⟩. ⟨hal-04164841⟩
70 Consultations
27 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More